Stainless steel: resistant to air, steam, water, and other weak corrosive media or stainless steel. The commonly used steel grades are 304, 304L, 316, and 316L, which are 300-series steels of austenitic stainless steel.
304 stainless steel:
Performance introduction:
304 stainless steel is the most common steel type. As a widely used steel, it has good corrosion resistance, heat resistance, low-temperature strength, and mechanical properties; it has good hot workability such as stamping and bending, and has no heat treatment hardening phenomenon (non-magnetic, then use the temperature -196 ° C ~ 800 ° C).
Scope of application:
Household goods (Class 1 and Class 2 tableware, cabinets, indoor pipelines, water heaters, boilers, bathtubs)
Auto parts (windshield wipers, mufflers, moldings)
Medical equipment, building materials, chemistry, food industry, agriculture, ship parts, etc.
304L stainless steel (L is low carbon):
Performance introduction:
As a low-carbon 304 steel, its corrosion resistance is similar to that of 304 steel under normal conditions, but after welding or stress relief, its resistance to intergranular corrosion is excellent; it can also maintain good corrosion resistance without heat treatment. Excellent corrosion resistance, service temperature -196 ° C ~ 800 ° C.
Scope of application:
Applied to field machines in the chemical, coal, and petroleum industries that require high resistance to grain boundary corrosion, heat-resistant parts of building materials, and parts that are difficult to heat treat.
316 stainless steel:
Performance introduction:
Due to the addition of molybdenum, 316 stainless steel has particularly good corrosion resistance, atmospheric corrosion resistance, and high-temperature strength, and can be used under harsh conditions; it has excellent work hardening (non-magnetic).
Scope of application:
Equipment used in seawater, chemical, dye, paper, oxalic acid, fertilizer, and other production equipment; photography, food industry, coastal area facilities, ropes, CD rods, bolts, and nuts.
316L stainless steel (L is low carbon):
Performance introduction
As a low-carbon series of 316 steel, in addition to having the same characteristics as 316 steel, it has excellent resistance to intergranular corrosion.
Scope of application
Products with special requirements for grain boundary corrosion resistance.
Performance comparison
316 and 316L stainless steel are molybdenum-containing stainless steel species. The molybdenum content in 316L stainless steel is slightly higher than that of 316 stainless steel. Due to the molybdenum in the steel, the overall performance of this steel is better than that of 310 and 304 stainless steel. Under high-temperature conditions, when the concentration of sulfuric acid is lower than 15% and higher than 85%, 316 Stainless steel has a wide range of uses. 316 stainless steel also has good resistance to chloride attack, so it is usually used in marine environments. 316L stainless steel has a maximum carbon content of 0.03 and can be used in applications where annealing after welding is not possible and where maximum corrosion resistance is required.
Corrosion resistance
The corrosion resistance of 316 stainless steel is better than that of 304 stainless steel, and it has good corrosion resistance in the production process of pulp and paper. Moreover, 316 stainless steel is also resistant to erosion by marine and aggressive industrial atmospheres.
Generally speaking, there is not much difference between 304 stainless steel and 316 stainless steel in terms of chemical corrosion resistance, but there are differences in some specific media.
The stainless steel originally developed is 304, and under certain circumstances, this material is more sensitive to pitting corrosion (PittingCorrosion). Adding an extra 2-3% molybdenum reduces this sensitivity, and thus 316 is born. In addition, this extra molybdenum can reduce the corrosion of some hot organic acids.
316 stainless steel has almost become a standard material in the food and beverage industry. Due to the worldwide shortage of molybdenum and the higher nickel content in 316 stainless steel, 316 stainless steel is more expensive than 304 stainless steel.
Pitting corrosion is a phenomenon mainly caused by deposition corrosion on the surface of stainless steel, which cannot form a protective layer of chromium oxide due to a lack of oxygen.
Especially in small valves, the possibility of deposits on the valve plate is very small, so pitting corrosion is also rare.
In various types of water media (distilled water, drinking water, river water, boiler water, seawater, etc.), the corrosion resistance of 304 stainless steel and 316 stainless steel is almost the same, unless the content of chloride ions in the medium is very high, then 316 stainless steel will be more suitable.
In most cases, there is not much difference between the corrosion resistance of 304 stainless steel and 316 stainless steel, but in some cases, it may be very different, which needs to be analyzed in detail. Generally speaking, valve users should know it well, because they will choose the material of containers and pipes according to the conditions of the medium, and it is not recommended to recommend materials to users.
Heat resistance:
In intermittent use below 1600 degrees and continuous use below 1700 degrees, 316 stainless steel has good oxidation resistance. In the range of 800-1575 degrees, it is best not to use 316 stainless steel continuously, but when 316 stainless steel is used continuously outside this temperature range, the stainless steel has good heat resistance. The carbide precipitation resistance of 316L stainless steel is better than that of 316 stainless steel, and the above temperature range can be used.
Heat treatment:
Annealing is carried out in the temperature range of 1850-2050 degrees, followed by rapid annealing and rapid cooling. 316 stainless steel cannot be hardened by heat treatment.
Welding:
316 stainless steel has good welding performance. All standard welding methods can be used for welding. According to the application, 316Cb, 316L, or 309Cb stainless steel filler rods or welding rods can be used for welding. To obtain the best corrosion resistance, the welded section of 316 stainless steel needs to be annealed after welding. If 316L stainless steel is used, post-weld annealing is not required.
Mechanical behavior:
Of all steels, austenitic stainless steels have the lowest yield point. Therefore, in terms of mechanical properties, austenitic stainless steel is not the best material for the valve stem, because to ensure a certain strength, the diameter of the valve stem will increase. The yield point cannot be increased by heat treatment, but it can be increased by cold forming.
Magnetic:
Due to the wide application of austenitic stainless steel, people have the wrong impression that all stainless steels are not magnetic. Austenitic stainless steel can be understood as non-magnetic, and it is true for quenched forged steel. But 304 processed by cold forming will be somewhat magnetic. For cast steel, if it is 100% austenitic stainless steel, it is not magnetic.
Low Carbon Types of Stainless Steel:
The corrosion resistance of austenitic stainless steel comes from the protective chromium oxide layer formed on the metal surface. If the material is heated to a high temperature of 450°C to 900°C, the structure of the material changes, and chromium carbides form along the crystal edges. In this way, a protective layer of chromium oxide cannot be formed at the edge of the crystal, resulting in reduced corrosion resistance. This corrosion is called “intergranular corrosion”.
As a result, 304L stainless steel and 316L stainless steel were developed to resist this corrosion. Both 304L stainless steel and 316L stainless steel have low carbon content. Because the carbon content is reduced, chromium carbide will not be produced, and intergranular corrosion will not occur.
It should be noted that higher susceptibility to intergranular corrosion does not mean that non-low carbon materials are more prone to corrosion. This sensitivity is also increased in high-chlorine environments.
Please note that this phenomenon is due to high temperatures (450°C-900°C). Usually soldering is the direct cause of reaching this temperature. For soft seat conventional butterfly valves it doesn’t make much sense to go with low carbon stainless since we don’t do welding on the plate, but most specs will call for 304L or 316L.
Similar Articles:
- 304 stainless steel
- Stainless steel casting
- Stainless steel knowledge
- Carbon steel VS stainless steel
- Process flow of stainless steel precision casting
- Classification and performance of stainless steel grades